Ribbon is a commonly used item in our daily lives, commonly used in various industries such as clothing, shoe materials, luggage, industry, agriculture, military supplies, transportation, etc. According to different needs, there are various types of webbing. Below is an overview of the commonly used materials for webbing.
1. Pure cotton webbing
Generally used without safety requirements, trademark straps, clothing accessories, handbags, sports equipment, medical supplies, texture: soft physical properties: natural cotton, softness: good, strength: worse than nylon yarn, Teflon yarn, PP yarn, acrylic yarn, dyeing: after dyeing (water dyeing), water-based dyes, room temperature dyeing about 80-100 degrees destructive: self decay, environmentally friendly cutting, characteristics: good water absorption, natural raw materials, No environmental issues.
2. Tendo yarn (also known as polyester yarn)
The main raw materials for producing polyester webbing are: (Teduo 300D twisted yarn is mostly used for high-speed elastic belts, Teduo 150D raw yarn is mostly used for knitted elastic belts) The small yarn and weft of jacquard ribbons are from coarse to fine: 1200D, 900D, 600D, 300D, 150D, and their properties are twisted and untwisted (AO raw yarn). When Teduo yarn is used for weft yarn, it does not need to be twisted. Twisted yarn: When making webbing, it is not easy to fuzz, and when used for small yarns, it is necessary to use twisted yarn to prevent fuzzing, which will emit black smoke when burned.
3. PP webbing
Generally used for handbags that do not involve safety requirements. The amount used is * * Texture: slightly harder than nylon yarn Physical properties: softer than nylon yarn Strength: worse than nylon yarn Dyeability: front dyeing (added before molding) Pigment destructive: sun erosion and natural decomposition characteristics: self decay, environmentally friendly cutting.
4. Nylon webbing
Generally used for safety requirements, such as general seat belts. Texture: Soft properties are the same as that of Teflon yarn. Physical properties: Good softness, strength: lower than Teflon yarn, higher than PP yarn, Teflon yarn, acrylic yarn, pure cotton yarn. Dyeability: after dyeing (water dyeing), room temperature dyeing at about 80-100 degrees. Destructive: not subject to sunlight erosion, but can be corroded by hydrochloric acid. Characteristics: wear resistance and high tensile strength.